Methods for reducing aldehyde emissions in polyurethane foams

ABSTRACT

Polyurethane foams are made by curing a reaction mixture that contains an aromatic polyisocyanate, at least one isocyanate-reactive material having an average functionality of at least 2 and an equivalent weight of at least 200 per isocyanate-reactive group, at least one blowing agent, at least one surfactant and at least one catalyst, at least one cyclic 1,3-diketone compound, at least one aminoalcohol or alkylhydroxylamine and an alkali metal, phosphonium or ammonium sulfite. Foams so produced emit low levels of formaldehyde, acetaldehyde, acrolein and propionaldehyde.

This invention relates to polyurethanes that exhibit low levels of aldehyde emissions, and to methods for producing such polyurethanes.

Polyurethane foams are used in many office, household and vehicular applications. They are used, for example, in appliance applications and as cushioning for bedding and furniture. In automobiles and trucks, polyurethanes are used as seat cushioning, in headrests, in dashboards and instrument panels, in armrests, in headliners, and other applications.

These polyurethanes often emit varying levels of aldehydes such as formaldehyde, acetaldehyde, acrolein (propenyl aldehyde) and propionaldehyde. Because of the cellular structure of these foams, aldehydes contained in the foam easily escape into the atmosphere. This can present an odor concern and an exposure concern, especially when people or animals are exposed to the material within an enclosed space. Vehicle manufacturers are imposing stricter limits on the emissions from materials that are used in the passenger cabins of cars, trucks, trains and aircraft.

Scavengers are sometimes used to reduce aldehyde emissions from various types of materials. In the polyurethane field, there is, for example, WO 2006/111492, which describes adding antioxidants and hindered amine light stabilizers (HALS) to polyols to reduce aldehydes. WO 2009/114329 describes treating polyols with certain types of aminoalcohols and treating polyisocyanates with certain nitroalkanes, in order to reduce aldehydes in the polyols and polyisocyanates, respectively, and in polyurethanes made from those materials. JP 2005-154599 describes the addition of an alkali metal borohydride to a polyurethane formulation for that purpose. U.S. Pat. No. 5,506,329 describes the use of certain aldimine oxazolidine compounds for scavenging formaldehyde from polyisocyanate-containing preparations, and describes nitroalkanes and aminoalcohols as formaldehyde scavengers in textile and plywood applications.

These approaches provide limited benefit, in part because aldehydes present in polyurethane foam are not always carried in from the raw materials used to make the foam. Formaldehyde and acetaldehyde in particular can form during the curing step or when the foam is later subjected to UV light, elevated temperatures or other conditions. In addition, measures that are effective against formaldehyde emissions are not always effective against acetaldehyde, acrolein or propionaldehyde emissions, and vice versa. In some cases, measures that are effective in reducing acetaldehyde emissions can actually cause an increase in formaldehyde emissions. Applicants have further found that the presence of HALS often leads to an increase in formaldehyde emissions, acetaldehyde emissions or both.

PCT/CN2017/073764 describes the use of aminoalcohols together with certain antioxidants to reduce aldehyde emissions from polyurethane foam. This combination provides some improvement, but a greater reduction of aldehyde emissions is wanted.

Therefore, a method for effectively and economically reducing formaldehyde, acetaldehyde, acrolein and propionaldehyde emissions is wanted. Preferably, this method does not result in a significant change in the properties or performance of the polyurethane.

This invention is a process for producing a polyurethane foam comprising forming a reaction mixture that contains an aromatic polyisocyanate, at least one isocyanate-reactive material having an average functionality of at least 2 and an equivalent weight of at least 200 per isocyanate-reactive group, at least one blowing agent, at least one surfactant and at least one catalyst, and curing the reaction mixture in the presence of (i) at least one cyclic 1,3-diketone, (ii) at least one aminoalcohol and/or alkylhydroxylamine and (iii) an alkali metal, ammonium or phosphonium sulfite, to form the polyurethane foam.

The invention is also a process for reducing aldehyde emissions from a polyurethane foam, comprising: a) combining (i) at least one cyclic 1,3-diketone compound, (ii) at least one aminoalcohol and/or alkylhydroxylamine compound and (iii) an alkali metal, ammonium or phosphonium sulfite with at least one isocyanate-reactive material having an average functionality of at least 2 and an equivalent weight of at least 200 per isocyanate-reactive group to form a mixture and then b) combining the mixture from step a) with at least one organic polyisocyanate and curing the resulting reaction mixture in the presence of at least one blowing agent, at least one surfactant and at least one catalyst to form a polyurethane foam.

The invention is also a polyurethane foam made in either of the foregoing processes.

The combination of the cyclic diketone, aminoalcohol and/or hydroxylamine and alkali metal, ammonium or phosphonium sulfite has been found to reduce the levels of each of formaldehyde, acetaldehyde, acrolein and propionaldehyde emitted by the polyurethane foam.

To produce foam in accordance with the invention, at least one polyisocyanate is reacted with at least one isocyanate-reactive compound that has a functionality of at least 2 and an equivalent weight of at least 200 per isocyanate-reactive group. Other ingredients may be present as discussed hereinbelow. The reaction is performed in the presence of the cyclic 1,3-diketone, the aminoalcohol and/or hydroxylamine and the alkali metal, ammonium or phosphonium sulfite.

The cyclic 1,3-diketone, aminoalcohol and/or hydroxylamine and alkali metal, ammonium or phosphonium sulfite can be provided as a mixture with any one or more of the various ingredients of the formulation used to produce the foam. Alternatively, these may be added into the reaction as a separate component or stream without being previously combined with any of the other ingredients.

Preferably, however, the cyclic 1,3-diketone, aminoalcohol and/or hydroxylamine and alkali metal, ammonium or phosphonium sulfite are blended with the isocyanate reactive compound(s) that have at least two isocyanate-reactive groups per molecule and an equivalent weight of at least 200 per isocyanate-reactive group, prior to forming the polyurethane foam. The resulting blend is maintained at approximately room temperature or a higher temperature (but below the boiling temperature of the cyclic 1,3-diketone and the aminoalcohol and/or hydroxylamine and below the temperature at which the polyol degrades) for a period of at least 30 minutes prior to making the foam. Such a blend may be maintained under such conditions for any arbitrarily longer time, such as up to a month, up to a week, or up to a day.

The cyclic 1,3-diketone is characterized in having two carbonyl groups in the beta-position with respect to each other. Such 1,3-diketones are known and described, for example, in DE3037912A1; US20050054757A1; JP2005082694A; JP2005162921A; JP2005162920A; CN103897567A; WO2010039485A1; FR2940273A1; WO2010070248A2, all of which are incorporated herein in their entirety. The cyclic 1,3-diketone compound is preferably is characterized in having at least one:

moiety as part of a ring. The ring may contain, for example, 4, 5 or 6 ring atoms. The ring atoms (other than the atoms of 1,3-dikeone structure I that form part of the ring) may be, for example, carbon, nitrogen and/or oxygen atoms.

Among the suitable cyclic 1,3-diketones are compounds represented by structure II

wherein X, Y, Z are independently carbonyl, —C(R²R³)—, —NR⁴—, —O— or a chemical bond, each R² and R³ are independently H, a substituted or unsubstituted linear or branched alkyl or alkenyl group having 1 to 10 carbon atoms, a substituted or unsubstituted phenyl group, a halogen, —CO₂CH₃, or —CN, with the proviso that any two or more of R² and R³ may be connected intra- or inter-molecularly, and each R⁴ is independently H, a substituted or unsubstituted linear or branched alkyl or alkenyl group having 1 to 10 carbon atoms or a substituted or unsubstituted phenyl group.

Other suitable cyclic 1,3-diketone compounds are represented by structure III:

wherein Z is carbonyl, —C(R²R³)—, —NR⁴—, —O— or a chemical bond, each R² and R³ are independently H, a substituted or unsubstituted linear or branched alkyl or alkenyl group having 1 to 10 carbon atoms, a substituted or unsubstituted phenyl group, a halogen, —CO₂CH₃, or —CN, with the proviso that any two or more of R² and R³ may be connected intra- or inter-molecularly and each R⁴ is independently H, a substituted or unsubstituted linear or branched alkyl or alkenyl group having 1 to 10 carbon atoms or a substituted or unsubstituted phenyl group.

R², R³ and R⁴, when substituted, preferably are substituted with only nitrogen and/or oxygen atoms. Oxygen substituents may be, for example, may be ether, carbonyl or hydroxyl oxygens. Nitrogen substituents may be primary or secondary amino, imido or amido nitrogens.

Specific cyclic 1,3-diketones include, for example, cyclohexane-1,3,5-trione, 1,3-cyclohexanedione, pyrazolidine-3,5-dione, 1,2-dimethylpyrazolidine-3,5-dione, 1-methylpyrazolidine-3,5-dione, 1,1-dimethyl-cyclopentan-2,4-dione, 1-ethyl-cyclohexan-2,4-dione, 1,1-diethyl-cyclohexan-3,5-dione, 6-methyl-pyran-2,4-dione, 6-ethyl-pyran-2,4-dione, 6-isopropyl-pyran-2,4-dione, 6-(n)-butyl-pyran-2,4-dione, 6-isobutyl-pyran-2,4-dione, 6-pentyl-pyran-2,4-dione, 6-isopentyl-pyran-2,4-dione, 6,7-dihydrocyclopenta[b]pyran-2,4(3H,5H)-dione, 5,6,7,8-tetrahydro-chroman-2,4-dione, chroman-2,4-dione, 6-trans-propenyl-dihydro-pyran-2,4-dione, 1-oxaspiro-[5,5]-undecan-2,4-dione, 2,2-dipropyl-[1,3]-dioxan-4,6-dione, 2-phenyl-[1,3]-dioxan-4,6-dione, 6,10-dioxa-spiro-[4,5]-decan-7,9-dione, 1,5-dioxa-spiro-[5,5]-undecan-2,4-dione, 1-methyl-2,4,6-trioxo-hexahydro-pyrimidine, 1-ethyl-2,4,6-trioxo-hexahydro-pyrimidine, 1-phenyl-2,4,6-trioxo-hexahydro-pyrimidine, s-indacene-1,3,5,7(2H,6H)-tetraone, furan-2,4(3H,5H)-dione, 3,3′-(hexane-1,1-diyl)bis(1-methylpyrimidine-2,4,6(1H,3H,5H)-trione), 2,2-dimethyl-1,3-dioxane-4,6-dione, furan-2,4(3H,5H)-dione, pyrimidine-2,4,6(1H,3H,5H)-trione and 1,3-dimethylpyrimidine-2,4,6(1H,3H,5H)-trione.

A suitable amount of cyclic 1,3-diketone is from 0.01 to 5 pph (i.e., 0.10 to 5 parts by weight per 100 parts by weight of isocyanate reactive compound(s) that have at least two isocyanate-reactive groups per molecule and an equivalent weight of at least 200 per isocyanate-reactive group). The amount of cyclic 1,3-diketone may be at least 0.02, at least 0.03 pph or at least 0.04 pph and may be up to 2 pph, up to 1 pph, up to 0.5 pph, up to 0.25 pph, up to 0.15 pph or up to 0.1 pph.

Aminoalcohols are characterized in having at least one primary or secondary amino group and at least one hydroxyl group, each being bonded to an aliphatic carbon atom. In some embodiments, a hydroxyl group is bonded to a carbon in the alpha position relative to the carbon atom to which a primary or secondary amino group is bonded. An alkylhydroxylamine includes an —NH—OH group wherein the nitrogen atom is bonded to an aliphatic carbon atom.

Aminoalcohols are known and include for example, those described in US Publication Nos. 2009/0227758 and 2010/0124524, each of which are incorporated herein in their entirety.

In some embodiments, the aminoalcohol or alkylhydroxylamine is represented by structure IV:

or a salt of such a compound, wherein

R⁶, R⁷ and R⁸ each are independently H, alkyl optionally substituted with phenyl or NR⁹R¹⁰ wherein R⁹ and R¹⁰ are independently H, C₁-C₆ alkyl, phenyl, or hydroxyalkyl optionally independently substituted with phenyl or NR⁹R¹⁰;

R⁵ is H, hydroxyl, phenyl, alkyl optionally substituted with phenyl or NR⁹R¹⁰, or hydroxyalkyl optionally independently substituted with phenyl or NR⁹R¹⁰, provided that when none of R⁶, R⁷ and R⁸ are hydroxyalkyl, then R⁵ is hydroxyl or hydroxyalkyl optionally independently substituted with phenyl or NR⁹R¹⁰.

Specific examples of suitable aminoalcohols are 2-amino-1-butanol, 2-amino-2-ethyl-1,3-propanediol, 2-amino-2-methyl-1-propanol, 2-amino-1-methyl-1,3-propanediol, 1,1,1-tris (hydroxymethyl) methylamine, ethanolamine, diethanolamine, N-methylethanolamine, N-butylethanolamine, monoisopropanolamine, 2-amino-2(hydroxymethyl)propane-1,3-diol. diisopropanolamine, mono-sec-butanolamine, di-sec-butanolamine, or salts thereof. These aminoalcohols are available from a variety of commercial sources, including ANGUS Chemical Company (Buffalo Grove, Ill., USA), The Dow Chemical Company (Midland, Mich., USA), or can be readily prepared by techniques well known in the art. The aminoalcohols can be used in the form of salts. Suitable salts include hydrochloride, acetate, formate, oxalate, citrate, carbonate, sulfate, and phosphate salts.

Specific examples of alkylhydroxylamines include N-isopropylhydroxylamine, N-ethylhydroxylamine, N-methylhydroxylamine, N-(n-butyl)hydroxylamine, N-(sec-butyl)hydroxylamine and the like.

A suitable amount of aminoalcohol and/or alkylhydroxylamine compound is from 0.01 to 5 pph. The amount of aminoalcohol and/or alkylhydroxylamine compound may be at least 0.025, at least 0.05 pph or at least 0.075 pph and may be up to 2 pph, up to 1 pph, up to 0.5 pph, up to 0.25 pph or up to 0.2 pph.

The alkali metal, ammonium or phosphonium sulfite includes compounds having the formula A₂SO₃, where A represents alkali metal, ammonium or phosphonium, and alkali metal, ammonium or phosphonium hydrogen sulfite (alkali metal, ammonium or phosphonium bisulfite) compounds having the formula AHSO₃, where A is as before. Examples of such compounds include, for example, dilithium sulfite, disodium sulfite, dipotassium sulfite, di(tetramethyl ammonium) sulfite, di(tetramethyl phosphonium) sulfite, lithium hydrogen sulfite (LiHSO₃), sodium hydrogen sulfite (NaHSO₃), potassium hydrogen sulfite (KHSO₃), cesium hydrogen sulfite (CsHSO₃), (tetramethyl ammonium) hydrogen sulfite, (tetramethyl phosphonium) hydrogen sulfite, with the sodium compounds being preferred among these. A suitable amount of alkali metal, ammonium or phosphonium sulfite is from 0.01 to 5 pph. The amount of alkali metal, ammonium or phosphonium sulfite may be at least 0.02 pph, at least 0.025 pph or at least 0.05 pph and may be up to 2 pph, up to 1 pph, up to 0.5 pph, up to 0.25 pph or up to 0.2 pph.

The foam formulation includes at least one isocyanate-reactive compound that has a functionality of at least 2 and an equivalent weight of at least 200 per isocyanate-reactive group. “Functionality” refers to the average number of isocyanate-reactive groups per molecule. The functionality may be as much as 8 or more but preferably is from 2 to 4. The isocyanate groups may be, for example, hydroxyl, primary amino or secondary amino groups, but hydroxyl groups are preferred. The equivalent weight may be up to 6000 or more, but is preferably from 500 to 3000 and more preferably from 1000 to 2000. This isocyanate-reactive compound may be, for example, a polyether polyol, a polyester polyol, a hydroxyl-terminated butadiene polymer or copolymer, a hydroxyl-containing acrylate polymer, and the like. A preferred type of isocyanate-reactive compound is a polyether polyol, especially a polymer of propylene oxide or a copolymer of propylene oxide and ethylene oxide. A copolymer of propylene oxide and ethylene oxide may be a block copolymer having terminal poly(oxyethylene) blocks and in which at least 50% of the hydroxyl groups are primary. Another suitable copolymer of propylene oxide and ethylene oxide may be a random or pseudo-random copolymer, which may also contain terminal poly(oxyethylene) blocks and in which at least 50% of the hydroxyl groups are primary.

Polyester polyols that are useful as the isocyanate-reactive compound include reaction products of polyols, preferably diols, with polycarboxylic acids or their anhydrides, preferably dicarboxylic acids or dicarboxylic acid anhydrides. The polycarboxylic acids or anhydrides may be aliphatic, cycloaliphatic, aromatic and/or heterocyclic and may be substituted, such as with halogen atoms. The polycarboxylic acids may be unsaturated. Examples of these polycarboxylic acids include succinic acid, adipic acid, terephthalic acid, isophthalic acid, trimellitic anhydride, phthalic anhydride, maleic acid, maleic acid anhydride and fumaric acid. The polyols used in making the polyester polyols preferably have an equivalent weight of about 150 or less and include ethylene glycol, 1,2- and 1,3-propylene glycol, 1,4- and 1,3-butane diol, 1,6-hexane diol, 1,8-octane diol, neopentyl glycol, cyclohexane dimethanol, 2-methyl-1,3-propane diol, glycerine, trimethylolpropane, 1,2,6-hexane triol, 1,2,4-butane triol, trimethylolethane, pentaerythritol, quinitol, mannitol, sorbitol, methyl glycoside, diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, dibutylene glycol and the like. Polycaprolactone polyols such as those sold by The Dow Chemical Company under the trade name “Tone” are also useful.

Mixtures of two or more of the foregoing isocyanate-reactive compounds having a functionality of at least 2 and an equivalent weight of at least 200 per isocyanate-reactive group can be used if desired.

The isocyanate-reactive compound(s) may contain dispersed polymer particles. These so-called polymer polyols contain, for example, particles of vinyl polymers such as styrene, acrylonitrile or styrene-acrylonitrile, particles of a polyurea polymer, or polymers of a polyurethane-urea polymer.

In addition, such isocyanate-reactive compounds can be used in admixture with one or more crosslinkers and/or chain extenders. For purposes of this specification, “crosslinkers” are compounds having at least three isocyanate-reactive groups per molecule and an equivalent weight per isocyanate-reactive group of below 200. “Chain extenders” for purposes of this invention have exactly two isocyanate-reactive groups per molecule and have an equivalent weight per isocyanate-reactive group of below 200. In each case, the isocyanate-reactive groups are preferably hydroxyl, primary amino or secondary amino groups. Crosslinkers and chain extenders preferably have equivalent weights of up to 150 and more preferably up to about 125.

Examples of crosslinkers include glycerin, trimethylolpropane, trimethylolethane, diethanolamine, triethanolamine, triisopropanolamine, alkoxylates of any of the foregoing that have equivalent weights of up to 199, and the like. Examples of chain extenders include alkylene glycols (e.g., ethylene glycol, propylene glycol, 1,4-butane diol, 1,6-hexanediol and the like), glycol ethers (such as diethylene glycol, triethylene glycol, dipropylene glycol, tripropylene glycol and the like), ethylene diamine, toluene diamine, diethyltoluene diamine and the like, as well as alkoxylates of any of the foregoing that have equivalent weights of up to 199, and the like.

Crosslinkers and/or chain extenders are typically present in small amounts (if at all). A preferred amount is from 0 to 5 pph of crosslinkers and/or chain extenders. A more preferred amount is from 0.05 to 2 pph and a still more preferred amount is from 0.1 to 1 pph of one or more crosslinkers.

Examples of suitable polyisocyanates include, for example, m-phenylene diisocyanate, 2,4- and/or 2,6-toluene diisocyanate (TDI), the various isomers of diphenylmethanediisocyanate (MDI), the so-called polymeric MDI products (which are a mixture of polymethylene polyphenylene polyisocyanates in monomeric MDI), carbodiimide-modified MDI products (such as the so-called “liquid MDI” products which have an isocyanate equivalent weight in the range of 135-170), hexamethylene-1,6-diisocyanate, tetramethylene-1,4-diisocyanate, cyclohexane-1,4-diisocyanate, hexahydrotoluene diisocyanate, hydrogenated MDI (H₁₂MDI), isophorone diisocyanate, naphthylene-1,5-diisocyanate, methoxyphenyl-2,4-diisocyanate, 4,4′-biphenylene diisocyanate, 3,3′-dimethyoxy-4,4′-biphenyl diisocyanate, 3,3′-dimethyldiphenyl methane-4,4′-diisocyanate, 4,4′,4″-triphenylmethane diisocyanate, hydrogenated polymethylene polyphenylpolyisocyanates, toluene-2,4,6-triisocyanate and 4,4′-dimethyldiphenylmethane-2,2′,5,5′-tetraisocyanate. Any of the foregoing that is modified to contain urethane, urea, uretonimine, biuret, allophonate and/or carbodiimide groups may be used.

Preferred isocyanates include TDI, MDI and/or polymeric MDI, as well as derivatives of MDI and/or polymeric MDI that contain urethane, urea, uretonimine, biuret, allophonate and/or carbodiimide groups. An especially preferred isocyanate is a mixture of TDI and MDI.

The amount of polyisocyanate provided to the foam formulation is expressed as the “isocyanate index”, which is 100 times the ratio of isocyanate groups to isocyanate-reactive groups in the foam formulation. The isocyanate index is typically from about 70 to 150. A preferred isocyanate index is from 80 to 125 and a more preferred isocyanate index is from 80 to 115. In some embodiments, the isocyanate index is from 90 to 115 or from 95 to 115.

The blowing agent may be a chemical (exothermic) type, a physical (endothermic) type or a mixture of at least one of each type. Chemical types typically react or decompose to produce carbon dioxide or nitrogen gas under the conditions of the foaming reaction. Water and various carbamate compounds are examples of suitable chemical blowing agents. Physical types include carbon dioxide, various low-boiling hydrocarbons, hydrofluorocarbons, hydroflurochlorocarbons, ethers and the like. Water is most preferred blowing agent, either by itself or in combination with one or more physical blowing agents.

Blowing agents are present in amounts sufficient to provide the desired foam density. When water is the blowing agent, a suitable amount is generally from 1.5 to 6 pph, preferably from 2 to 5 pph.

Suitable surfactants are materials that help to stabilize the cells of the foaming reaction mixture until the materials have cured. A wide variety of silicone surfactants as are commonly used in making polyurethane foams can be used in making the foams with the polymer polyols or dispersions of this invention. Examples of such silicone surfactants are commercially available under the tradenames Tegostab™ (Evonik Corporation), Niax™ (Momentive) and Dabco™ (Air Products and Chemicals).

Surfactants are typically present in amounts up to 5 pph, more typically from 0.1 to 2 pph and preferably from 0.25 to 1.5 pph.

Suitable catalysts include those described by U.S. Pat. No. 4,390,645, which is incorporated herein by reference. Representative catalysts include:

-   (a) tertiary amines, such as trimethylamine, triethylamine,     N-methylmorpholine, N-ethylmorpholine, N,N-dimethylbenzylamine,     N,N-dimethylethanolamine, N,N,N′,N′-tetramethyl-1,4-butanediamine,     N,N-dimethylp iperazine, 1,4-diazobicyclo-2,2,2-octane,     bis(dimethylaminoethyl)ether, bis(2-dimethylaminoethyl) ether,     morpholine,4,4′-(oxydi-2,1-ethanediyl)bis,     tri(dimethylaminopropyl)amine, pentamethyldiethylenetriamine and     triethylenediamine and the like; as well as so-called “low emissive”     tertiary amine catalysts that contain one or more     isocyanate-reactive groups such as dimethylaminepropylamine and the     like; -   (b) tertiary phosphines, such as trialkylphosphines and     dialkylbenzylphosphines; -   (c) chelates of various metals, such as those which can be obtained     from acetylacetone, benzoylacetone, trifluoroacetyl acetone, ethyl     acetoacetate and the like with metals such as Be, Mg, Zn, Cd, Pd,     Ti, Zr, Sn, As, Bi, Cr, Mo, Mn, Fe, Co and Ni; -   (d) acidic metal salts of strong acids, such as ferric chloride,     stannic chloride, stannous chloride, antimony trichloride, bismuth     nitrate and bismuth chloride; -   (e) strong bases, such as alkali and alkaline earth metal     hydroxides, alkoxides and phenoxides; -   (f) alcoholates and phenolates of various metals, such as Ti(OR)₄,     Sn(OR)₄ and Al(OR)₃, wherein R is alkyl or aryl, and the reaction     products of the alcoholates with carboxylic acids, beta-diketones     and 2-(N,N-dialkylamino)alcohols; -   (g) salts of organic acids with a variety of metals, such as alkali     metals, alkaline earth metals, Al, Sn, Pb, Mn, Co, Ni and Cu     including, for example, sodium acetate, stannous octoate, stannous     oleate, lead octoate, metallic driers, such as manganese and cobalt     naphthenate; and -   (h) organometallic derivatives of tetravalent tin, trivalent and     pentavalent As, Sb and Bi and metal carbonyls of iron and cobalt.

Catalysts are typically present in small amounts, such as up to 2 pph and generally up to 1 pph. A preferred amount of catalyst is from 0.05 to 1 pph.

It is preferred to produce the foam in the presence of at least one antioxidant. Such an antioxidant may be blended with the isocyanate reactive compound(s) that have at least two isocyanate-reactive groups per molecule and an equivalent weight of at least 200 per isocyanate-reactive group prior to forming the polyurethane foam, in the manner described above with regard to the cyclic 1,3-diketone, aminoalcohol and alkylhydroxylamine compounds. Alternatively, it may be added into the reaction mixture with one or more other ingredients and/or as a separate ingredient or stream.

Examples of suitable antioxidants include, for example:

-   1) Phenolic compounds such as 2,6-di-tert-butyl-4-methylphenol,     2-tert-butyl-4,6-dimethylphenol, 2,6-di-tert-butyl-4-ethylphenol,     2,6-di-tert-butyl-4-n-butylphenol,     2,6-di-tert-butyl-4-isobutylphenol,     2,6-dicyclopentyl-4-methylphenol,     2-(α-methylcyclohexyl)-4,6-dimethylphenol,     2,6-dioctadecyl-4-methylphenol, 2,4,6-tricyclohexylphenol,     2,6-di-tert-butyl-4-methoxymethylphenol, nonylphenols which are     linear or branched in the side chains, for example     2,6-di-nonyl-4-methylphenol,     2,4-dimethyl-6-(1′-methylundec-1′-yl)phenol,     2,4-dimethyl-6-(1′-methylheptadec-1′-yl)phenol,     2,4-dimethyl-6-(1′-methyltridec-1′-yl)phenol,     2,4-dioctylthiomethyl-6-tert-butylphenol,     2,4-dioctylthiomethyl-6-methylphenol,     2,4-dioctylthiomethyl-6-ethylphenol,     2,6-di-dodecylthiomethyl-4-nonylphenol,     2,6-di-tert-butyl-4-methoxyphenol, 2,5-di-tert-butylhydroquinone,     2,5-di-tert-amylhydroquinone, 2,6-diphenyl-4-octadecyloxyphenol,     2,6-di-tert-butylhydroquinone, 2,5-di-tert-butyl-4-hydroxyanisole,     3,5-di-tert-butyl-4-hydroxyanisole,     3,5-di-tert-butyl-4-hydroxyphenyl stearate,     bis(3,5-di-tert-butyl-4-hydroxyphenyl) adipate,     2,2′-methylenebis(6-tert-butyl-4-methylphenol),     2,2′-methylenebis(6-tert-butyl-4-ethylphenol),     2,2′-methylenebis[4-methyl-6-(α-methylcyclohexyl)phenol],     2,2′-methylenebis(4-methyl-6-cyclohexylphenol),     2,2′-methylenebis(6-nonyl-4-methylphenol),     2,2′-methylenebis(4,6-di-tert-butylphenol),     2,2′-ethylidenebis(4,6-di-tert-butylphenol),     2,2′-ethylidenebis(6-tert-butyl-4-isobutylphenol),     2,2′-methylenebis[6-(α-methylbenzyl)-4-nonylphenol],     2,2′-methylenebis[6-(α,α-dimethylbenzyl)-4-nonylphenol],     4,4′-methylenebis(2,6-di-tert-butylphenol),     4,4′-methylenebis(6-tert-butyl-2-methylphenol),     1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)butane,     2,6-bis(3-tert-butyl-5-methyl-2-hydroxybenzyl)-4-methylphenol,     1,1,3-tris(5-tert-butyl-4-hydroxy-2-methylphenyl)butane,     1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)-3-n-dodecylmercaptobutane,     ethylene glycol     bis[3,3-bis(3′-tert-butyl-4′-hydroxyphenyl)butyrate],     bis(3-tert-butyl-4-hydroxy-5-methyl-phenyl)dicyclopentadiene,     bis[2-(3′-tert-butyl-2′-hydroxy-5′-methylbenzyl)-6-tert-butyl-4-methylphenyl]terephthalate,     1,1-bis-(3,5-dimethyl-2-hydroxyphenyl)butane,     2,2-bis(3,5-di-tert-butyl-4-hydroxyphenyl)propane,     2,2-bis-(5-tert-butyl-4-hydroxy2-methylphenyl)-4-n-dodecylmercaptobutane,     1,1,5,5-tetra(5-tert-butyl-4-hydroxy-2-methylphenyl)pentane,     1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)-2,4,6-trimethylbenzene,     1,4-bis(3,5-di-tert-butyl-4-hydroxybenzyl)-2,3,5,6-tetramethylbenzene,     2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)phenol, esters of     β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid with mono- or     polyhydric alcohols, e.g. with methanol, ethanol, n-octanol,     i-octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene     glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol,     diethylene glycol, triethylene glycol, pentaerythritol,     tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide,     3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol,     trimethylolpropane,     4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane, esters     of β-(5-tert-butyl-4-hydroxy-3-methylphenyl)propionic acid with     mono- or polyhydric alcohols, e.g. with methanol, ethanol,     n-octanol, i-octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol,     ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene     glycol, diethylene glycol, triethylene glycol, pentaerythritol,     tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide,     3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol,     trimethylolpropane,     4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane;     3,9-bis[2-{3-(3-tert-butyl-4-hydroxy-5-methylphenyl)propionyloxy}-1,1-dimethylethyl]-2,4,8,10-tetraoxaspiro[5.5]-undecane,     esters of β-(3,5-dicyclohexyl-4-hydroxyphenyl)propionic acid with     mono- or polyhydric alcohols, e.g. with methanol, ethanol, octanol,     octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol,     1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene     glycol, triethylene glycol, pentaerythritol,     tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide,     3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol,     trimethylolpropane,     4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane, esters     of 3,5-di-tert-butyl-4-hydroxyphenyl acetic acid with mono- or     polyhydric alcohols, e.g. with methanol, ethanol, octanol,     octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol,     1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene     glycol, triethylene glycol, pentaerythritol,     tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide,     3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol,     trimethylolpropane,     4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane; -   2) Aminic antioxidants such as N,N′-di-isopropyl-p-phenylenediamine,     N,N′-di-sec-butyl-p-phenylenediamine,     N,N′-bis(1,4-dimethylpentyl)-p-phenylenediamine,     N,N′-bis(1-ethyl-3methylpentyl)-p-phenylenediamine,     N,N′-bis(1-methylheptyl)-p-phenylenediamine,     N,N′-dicyclohexyl-p-phenylenediamine,     N,N′-diphenyl-p-phenylenediamine,     N,N′-bis(2-naphthyl)-p-phenylenediamine,     N-isopropyl-N′-phenyl-p-phenylenediamine,     N-(1,3-dimethylbutyl)-N′-phenyl-p-phenylenediamine,     N-(1-methylheptyl)-N′-phenyl-p-phenylenediamine,     N-cyclohexyl-N′-phenyl-p-phenylenediamine,     4-(p-toluenesulfamoyl)diphenylamine,     N,N′-dimethyl-N,N′-di-sec-butyl-p-phenylenediamine, diphenylamine,     N-allyldiphenylamine, 4-isopropoxydiphenylamine,     N-phenyl-1-naphthylamine, N-(4-tert-octylphenyl)-1-naphthylamine,     N-phenyl-2-naphthylamine, octylated diphenylamine, for example     p,p′-di-tert-octyldiphenylamine, 4-n-butyl-aminophenol,     4-butyrylaminophenol, 4-nonanoylaminophenol,     4-dodecanoylaminophenol, 4-octadecanoylaminophenol,     bis(4-methoxyphenyl)amine,     2,6-di-tert-butyl-4-dimethylaminomethylphenol,     2,4′-diaminodiphenylmethane, 4,4′-diaminodiphenylmethane,     N,N,N′,N′-tetra-methyl-4,4′-diaminodiphenylmethane,     1,2-bis[(2-methylphenyl)amino]ethane, 1,2-bis(phenylamino)propane,     (o-tolyl)biguanide, bis[4-(1′,3′-dimethylbutyl)phenyl]amine,     tert-octylated N-phenyl-1-naphthylamine, a mixture of mono- and     dialkylated tert-butyl/tert-octyldiphenylamines, a mixture of mono-     and dialkylated nonyldiphenylamines, a mixture of mono- and     dialkylated dodecyldiphenylamines, a mixture of mono- and     dialkylated isopropyllisohexyldiphenylamines, a mixture of mono- and     dialkylated tert-butyldiphenylamines, and the like; -   3) Thiosynergists such as dilauryl thiodipropionate or distearyl     thiodipropionate; -   4) Phosphites and phosphonites such as triphenyl phosphite,     diphenylalkyl phosphites, phenyldialkyl phosphites,     tris(nonylphenyl) phosphite, trilauryl phosphite, trioctadecyl     phosphite, distearylpentaerythritol diphosphite,     tris(2,4-di-tert-butylphenyl) phosphite, diisodecyl pentaerythritol     diphosphite, bis(2,4-di-tert-butylphenyl)pentaerythritol     diphosphite, bis(2,4-di-cumylphenyl)pentaerythritol diphosphite,     bis(2,6-di-tert-butyl-4-methylphenyl)pentaerythritol diphosphite,     diisodecyloxypentaerythritol diphosphite,     bis(2,4-di-tert-butyl-6-methylphenyl)pentaerythritol diphosphite,     bis(2,4,6-tris(tert-butylphenyl)pentaerythritol diphosphite,     tristearyl sorbitol triphosphite, tetrakis(2,4-di-tert-butylphenyl)     4,4′-biphenylene diphosphonite,     6-isooctyloxy-2,4,8,10-tetra-tert-butyl-12H-dibenz[d,g]-1,3,2-dioxaphosphocin,     bis(2,4-di-tert-butyl-6-methylphenyl)methyl phosphite,     bis(2,4-di-tert-butyl-6-methylphenyl)ethyl phosphite,     6-fluoro-2,4,8,10-tetra-tert-butyl-12-methyl-dibenz[d,g]-1,3,2-dioxaphosphocin,     2,2′,2″-nitrilo-[triethyltris(3,3′,5,5′-tetra-tert-butyl-1,1′-biphenyl-2,2′-diyl)phosphite],     2-ethylhexyl(3,3′,5,5′-tetra-tert-butyl-1,1′-biphenyl-2,2′-diyl)phosphite,     5-butyl-5-ethyl-2-(2,4,6-tri-tert-butylphenoxy)-1,3,2-dioxaphosphirane; -   5) Benzofuranones and indolinones such as those disclosed in U.S.     Pat. Nos. 4,325,863; 4,338,244; 5,175,312; 5,216,052; 5,252,643;     DE-A-4316611; DE-A-4316622; DE-A-4316876; EP-A-0589839 or     EP-A-0591102, including for example     3-[4-(2-acetoxyethoxy)phenyl]-5,7-di-tert-butylbenzofuran-2-one,     5,7-di-tert-butyl-3-[4-(2-stearoyloxyethoxy)phenyl]-benzofuran-2-one,     3,3′-bis[5,7-di-tert-butyl-3-(4-[2-hydroxyethoxy]phenyl)benzofuran-2-one],     5,7-di-tert-butyl-3-(4-ethoxyphenyl)benzofuran-2-one,     3-(4-acetoxy-3,5-dimethylphenyl)-5,7-di-tert-butylbenzofuran-2-one,     3-(3,5-dimethyl-4-pivaloyloxyphenyl)-5,7-di-tert-butylbenzofuran-2-one,     3-(3,4-dimethylphenyl)-5,7-di-tert-butylbenzofuran-2-one,     3-(2,3-dimethylphenyl)-5,7-di-tert-burylbenzofuran-2-one, as well as -   6) tocophenols, hydroxylated thiodiphenyl ethers, O-, N- and     S-benzyl compounds, hydroxybenzylated malonates, triazine compounds,     benzylphosphonates, acylaminophenols, amides of     β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid, ascorbic acid     (vitamin C), 2-(2′-hydroxyphenyl)benzotriazoles,     2-hydroxybenzophenones, esters of substituted and unsubstituted     benzoic acids, acrylates, nickel compounds, oxamides,     2-(2-hydroxyphenyl)-1,3,5-triazines, hydroxylamines, nitrones,     esters of β-thiodipropionic acid, as described, for example, in U.S.     Pat. No. 6,881,774, incorporated herein by reference.

Preferred antioxidants include:

-   a) mixtures of at least one phenolic compound as described in 1)     above with at least one phosphite or phosphonite compound as     described in 4) above; -   b) mixtures of at least one phenolic compound as described in 1)     above with at least one benzofuranone or indolinone compound as     described in 5) above; -   c) mixtures of at least one phenolic compound as described in 1)     above with at least one aminic antioxidant as described in 2) above; -   d) mixtures of at least one phenolic compound as described in 1)     above with at least one phosphite or phosphonite compound as     described in 4) above and at least one benzofuranone or indolinone     compound as described in 5) above; -   e) mixtures of at least one phenolic compound as described in 1)     above with at least one phosphite or phosphonite compound as     described in 4) above and at least one aminic compound as described     in 2) above; -   f) mixtures of at least one phenolic compound as described in 1)     above with at least one phosphite or phosphonite compound as     described in 4) above, at least one benzofuranone or indolinone     compound as described in 5) above and at least one aminic compound     as described in 2) above; -   g) mixtures of at least one phenolic compound as described in 1)     above with at least one thiosynergist as described in 3); and -   h) any of mixtures a)-f) above with at least one thiosynergist as     described in 3).

The antioxidant(s), when used, is present in an effective amount, such as up to about 10 pph. A preferred amount is from 0.1 to 5 pph, and a more preferred amount is from 0.2 to 1.5 pph.

In some embodiments, a HALS (hindered amine light stabilizer) compound is present. Suitable HALS compounds include bis(1-octyloxy)-2,2,5,5-tetramethyl-4-piperidinyl) sebacate (Tinuvin™ 123 from BASF), n-butyl-(3,5-di-tert-butyl-4-hydroxylbenzyl)bis-(1,2,2,6-pentamethyl-4-piperidinyl)malonate (Tinuvin™ 144 from BASF), dimethyl succinate polymer with 4-hydroxy-2-2,6,6-tetramethyl-1-piperidinethanol (Tinuvin™ 622 from BASF), bis(1,2,2,6,6-pentamethyl-4-piperidinyl) sebacate (Tinuvin™ 765 from BASF) and bis(2,2,6,6-tetramethyl-4-piperidinyl) sebacate (Tinuvin™ 770 from BASF) and the like.

The HALS compound, when used, is present in an effective amount, such as up to about 10 pph in the aggregate. A preferred amount is from 0.1 to 5 pph in the aggregate, and a more preferred amount is from 0.1 to 2.5 pph.

Other ingredients may be present during the foaming step, including, for example, fillers, colorants, odor masks, flame retardants, biocides, antistatic agents, thixotropic agents and cell openers.

Polyurethane foam is made in accordance with this invention by forming a reaction mixture containing the various ingredients and curing the reaction mixture. Free-rise processes such as continuous slabstock production methods can be used. Alternatively, molding methods can be used. Such processes are well known. Generally, no alternation of conventional processing operations is needed to produce polyurethane foam in accordance with this invention (other than the inclusion of the cyclic-1,3-diketone, aminoalcohol and/or alkylhydroxylamine and alkali metal, ammonium or phosphonium sulfite and optionally the antioxidant(s) and/or HALS compound).

The various ingredients may be introduced individually or in various subcombinations into a mixhead or other mixing device where they are mixed and dispensed into a region (such as a trough or other open container, or a closed mold) where they are cured. It is often convenient, especially when making molded foam, to form a formulated polyol component that contains the isocyanate-reactive compound(s), including crosslinkers and/or chain extenders as may be used, the cyclic-1,3-diketone, aminoalcohol and/or alkylhydroxylamine, alkali metal, ammonium or phosphonium sulfite, the antioxidant(s) and HALS compounds (if any), and optionally the catalyst(s), surfactant(s) and blowing agent(s). This formulated polyol component is then contacted with the polyisocyanate (as well as any other ingredients that are not present in the formulated polyol component) to produce the foam.

Some or all of the various components may be heated prior to mixing them to form the reaction mixture. In other cases, the components are mixed at approximately ambient temperatures (such as from 15-40° C.). Heat may be applied to the reaction mixture after all ingredients have been mixed, but this is often unnecessary.

The product of the curing reaction is a flexible polyurethane foam. The foam density may be from 20 to 200 kg/m³. For most seating and bedding applications, a preferred density is from 24 to 80 kg/m³. The foam may have a resiliency of at least 50% on the ball rebound test of ASTM 3574-H. Foams produced in accordance with this invention are useful, for example, in cushioning applications such as bedding and domestic, office or vehicular seating, as well as in other vehicular applications such as headrests, dashboards instrument panels, armrests or headliners.

Polyurethane foams made in accordance with the invention are characterized in having reduced emissions formaldehyde, acetaldehyde, acrolein and propionaldehyde compared to the case in which the cyclic 1,3-diketone, aminoalcohol and/or alkylhydroxylamine and alkali metal, ammonium or phosphonium sulfite are absent. A suitable method for measuring formaldehyde, acetaldehyde, acrolein and propionaldehyde emissions is as follows: The polyurethane foam sample is crushed to open the cells. The crushed foam is cut into cubic 30 gram samples, which are immediately packaged tightly in aluminum foil or polyethylene film and kept in this manner for 5 days at about 25° C.

Aldehyde concentrations are measured according to the Toyota TSM0508G test method. In that Toyota method, the foam sample is removed from the foil or film and placed in individual 10 L Tedlar gas bags (Delin Co., Ltd., China) that has previously been purged three times with nitrogen gas. The bag with the foam sample is filled with 7 L of nitrogen, sealed and heated 65° C. for two hours. The plastic bag containing the foams is removed from the oven. The gas in the bag is pumped through a 350 mg dinitrophenylhydrazine cartridge to capture the carbonyl compounds. The captured carbonyl compounds are analyzed for formaldehyde, acetaldehyde, acrolein and propionaldehyde by liquid chromatography. Details for a specific method of performing the Toyota method are described in the following examples.

The amount of emitted formaldehyde, acetaldehyde, acrolein and propionaldehyde as determined by this method are all typically at least 20%, usually at least 50%, and sometimes as much as 80 to 98%, reduced as compared to an otherwise like foam that is produced in the absence of the cyclic 1,3-diketone, aminoalcohol and/or alkylhydroxylamine and alkali metal, ammonium or phosphonium sulfite. An advantage of this invention is that significant reductions are seen in the emitted amounts of all four of these aldehyde compounds.

In some embodiments, the amount of emitted formaldehyde and amount of emitted acrolein each are no greater than 10 μg/m³ or no greater than 5 μg/m³, as measured according to the Toyota method. In some embodiments, the amount of emitted acetaldehyde is no greater than 100 μg/m³, no greater than 50 μg/m³, or no greater than 35 μg/m³, as measured according to Toyota method. In some embodiments, the amount of emitted propionaldehyde is no greater than 60 μg/m³ or no greater than 50 μg/m³, as measured according to the Toyota method. The sum of emitted amounts of formaldehyde, acetaldehyde, acrolein and propionaldehyde in some embodiments is no greater than 150 μg/m³, no greater than 100 μg/m³, no greater than 75 μg/m³ or no greater than 50 μg/m³, as measured according to the Toyota method.

The following examples are provided to illustrate the invention, but are not intended to limit the scope thereof. All parts and percentages are by weight unless otherwise indicated.

EXAMPLE 1 AND COMPARATIVE SAMPLES A AND B

Formulated Polyol A is made by combining 45.34 parts of a glycerin-initiated poly(propylene oxide) capped with 15 percent ethylene oxide and having a hydroxyl number of 27.5 mg KOH/g; 50.11 parts of a copolymer polyol having a hydroxyl number of 22 mg KOH/g and containing 40 percent by weight copolymerized styrene and acrylonitrile solids dispersed in a polyether polyol; 0.48 part of diethanolamine, 0.38 part of glycerine, 0.27 part of a 33 percent triethylene diamine in dipropylene glycol, 0.17 part of a tertiary amine/glycol mixture available as C225 from Momentive Co., Ltd.; 1.15 parts of an organosilicone foam-stabilizing surfactant, 2.1 parts of water and 0.5 part of benzenepropanoic acid, 3,5-bis (1,1-dimethyl-ethyl)-4-hydroxy-C7-C9 branched alkyl esters (available as IRGANOX™ 1135 antioxidant from BASF (China) Co., Ltd).

Formulated Polyol B is made by combining 100.5 parts of Formulated Polyol A with 0.17 part of 1,3-cyclohexanedione and 0.3 part of 1,1,1-tris (hydroxymethyl) methylamine in a high speed laboratory mixer.

Formulated Polyol 1 is made by combining 100.5 parts of Formulated Polyol A with 0.17 part of 1,3-cyclohexanedione, 0.3 part of 1,1,1-tris (hydroxymethyl) methylamine and 0.1 part of sodium hydrogen sulfite (NaHSO₃) in a high speed laboratory mixer.

Each of Formulated Polyols A, B and 1 are stored at room temperature for 12-24 hours before being processed into a foam.

Comparative Sample A is made by combining 100 parts of Formulated Polyol A with 28 parts of a 20/80 by weight blend of toluene diisocyanate (TDI) and methylene diphenyldiisocyanate (MDI), pouring the resulting reaction mixture into a cup and allowing the reaction mixture to rise and cure to form a polyurethane foam. After the foam has cured enough to be dimensionally stable, it is removed from the cup and 30-gram sample cubes are cut. The foam cubes each are immediately wrapped in aluminum foil to form an airtight package for 7 days.

Comparative Sample B is made in the same manner, except 100 parts of Formulated Polyol B are combined with 28 parts of the same TDI/MDI blend.

Example 1 is made in the same manner, except 100 parts of Formulated Polyol 1 are combined with 28 parts of the same TDI/MDI blend.

Aldehydes emitted from the foam samples are analyzed using the Toyota gas bag method. The cubed foam samples are in each case removed from the foil and put into a 10 L Tedlar gas bag that has been washed with pure nitrogen three times and emptied. An empty gas bag is used as a blank. After the foam sample is put into the gas bag, the bag is filled with about 7 L of nitrogen gas and heated in the oven for 2 hours at 65° C. The nitrogen gas in the gas bag is then pumped out by an air pump and analyzed for formaldehyde, acetaldehyde, acrolein (propenyl aldehyde) and propionaldehyde.

The gas from each bag is passed through a dinitrophenylhydrazine (DNPH) cartridge (CNWBOND DNPH-Silica cartridge, 350 mg, Cat. No. SEEQ-144102, Anple Co., Ltd.) at a sampling speed is 330 mL/min. The aldehydes emitted from the foam into the gas are absorbed by the cartridge to form DNPH derivatives. The DNPH cartridge is eluted with 3 g of acetonitrile, and the resulting acetonitrile solution is analyzed by HPLC to quantify the carbonyls in the sample, as follows.

A standard solution containing 15 μg/mL each of formaldehyde, acetaldehyde, acrolein and propionaldehyde (in each case in the form of DNPH derivatives) (TO11A carbonyl-DNPH mix, Cat. No. 48149-U, Supelco Co., Ltd) is diluted with acetonitrile. A vial containing 2 mL of the diluted solution (containing 0.794 ppm of each of formaldehyde, acetaldehyde, acrolein and propionaldehyde) is refrigerated to −4° C. The refrigerated solution is injected into the HPLC system and analyzed for formaldehyde, acetaldehyde, acrolein and propionaldehyde derivatives. The response factor is calculated from the area of the elution peak for each derivative, according the formula:

${{Response}\mspace{14mu}{factor}\mspace{14mu} i} = \frac{{Peak}\mspace{14mu}{Area}\mspace{14mu} i}{0.794}$ where Response factor i=Response factor of derivative i; Peak Area i=Peak Area of derivative i in standard solution and 0.794=the concentration of each derivative in the standard solution.

The amounts of formaldehyde, acetaldehyde, acrolein and propionaldehyde emitted by each of Comparative Samples A and B and Example 1 are then determined. In each case, the acetonitrile solution obtained by eluting the DNPH column is injected into the HPLC system and the area of the elution peak is determined from each derivative. The concentration of the aldehyde-DNPH derivative in the sample solution is calculated as follows:

${{Concentration}\mspace{14mu}{of}\mspace{14mu} i} = \frac{{Peak}\mspace{14mu}{Area}\mspace{14mu} i}{{Response}\mspace{14mu}{factor}\mspace{14mu} i}$ where: Concentration of i=Concentration of aldehyde-DNPH derivative in the sample solution, Peak Area i=Peak Area of Derivative i in sample solution and Response factor i=Response factor of derivative i, determined from the standard solutions as described above.

The HPLC conditions are as follows:

Instrument: Agilent 1200 HPLC Column: Supelco Ascentis Express C18, 15 cm*4.6 mm, 2.7 um Mobile Phase: Solvent A: 0.1% H₃PO₄ in Acetonitrile Solvent B: 0.1% H₃PO₄ in DI water Column Oven: 15° C. Detection: DAD detector at 360 nm Time Flow Gradient: (mn) % A % B (mL/min) 0 45 55 1 7 45 55 1 14 50 50 1 20 85 15 1 25 100 0 1 Equilibration Time: 5 min Injection: 10 uL

The concentrations of formaldehyde, acetaldehyde, acrolein and propionaldehyde for each of Comparative Samples A and B and Example 1 are as indicated in Table 1.

TABLE 1 Comp. A* Comp. B* Ex. 1 Additives 0.5% IRGANOX 1135 0.5% IRGANOX 1135 0.5% IRGANOX 1135 0.3% 1,1,1- 0.3% 1,1,1- tris(hydroxymethyl) tris(hydroxymethyl) methylamine methylamine 0.17% 1,3-cyclohexanedione 0.17% 1,3-cyclohexanedione 0.1% NaHSO₃ Formaldehyde, 6 0 0 μg/m³ Acetaldehyde, 267 188 21 μg/m³ Acrolein, μg/m³ 23 13 0 Propionaldehyde, 302 111 45 μg/m³ Total Aldehydes, 598 312 66 μg/m³ *Not an example of this invention.

When the antioxidant is present by itself (Comp. A), acetaldehyde and propionaldehyde values in particular are quite high, as are total aldehydes. Further incorporating the 1,3-cyclohexandione and 1,1,1-tris(hydroxymethyl) methylamine into the foam formulation (Comp. B) reduces formaldehyde emissions to zero on this test, reduces acetaldehyde emissions by about 30%, reduces acrolein emissions by 45% and reduces propionaldehyde emissions by about two-thirds. Total aldehydes are reduced by nearly half. As this data shows, the combination of antioxidant, cyclic 1,3-diketone and aminoalcohol is already very effective at removing each of the measured aldehydes.

With the further addition of sodium hydrogen sulfite into Example 1, however, a much greater reduction in aldehyde emissions is seen, even compared with the good results of Comp. B. Formaldehyde and acrolein are reduced to zero. Acetaldehyde emissions are reduced by over 90%. Propionaldehyde emissions are reduced by 85%. Total aldehyde emissions are reduced by almost 90%.

EXAMPLES 2-3

Formulated Polyol 2 is made by combining 100.5 parts of Formulated Polyol A with 0.17 part of 1,3-cyclohexanedione, 0.3 parts of 1,1,1-tris (hydroxymethyl) methylamine and 0.05 part sodium hydrogen sulfite in a high speed laboratory mixer. 100 parts of Formulated Polyol 2 are reacted with 28 parts of the TDI/MDI mixture described before to make a cup foam.

Formulated Polyol 3 is made by combining 100 parts of Formulated Polyol A with 0.06 parts of 1,3-cyclohexanedione, 0.1 part of 1,1,1-tris (hydroxymethyl) methylamine and 0.1 part sodium hydrogen sulfite in a high speed laboratory mixer. 100.76 parts of Formulated Polyol 2 are reacted with 28 parts of the TDI/MDI mixture described before to make a cup foam.

The cup foams are made and tested in the manner described in the previous example. In addition, Comp. A and Example 1 are repeated and again tested. Results are as indicated in Table 2.

TABLE 2 Comp. A* Ex. 1 Ex. 2 Ex. 3 Additives 0.5% IRGANOX 1135 0.5% IRGANOX 1135 0.5% IRGANOX 1135 0.5% IRGANOX 1135 0.3% 1,1,1- 0.3% 1,1,1- 0.1% 1,1,1- tris(hydroxymethyl) tris(hydroxymethyl) tris(hydroxymethyl) methylamine methylamine methylamine 0.17% 1,3- 0.17% 1,3- 0.06% 1,3- cyclohexanedione cyclohexanedione cyclohexanedione 0.1% NaHSO₃ 0.05% NaHSO₃ 0.1% NaHSO₃ Formaldehyde, 12 0 0 0 μg/m³ Acetaldehyde, 125 5 34 13 μg/m³ Acrolein, μg/m³ 22 0 0 0 Propionaldehyde, 251 19 76 33 μg/m³ Total Aldehydes, 410 24 110 46 μg/m³ *Not an example of this invention.

As the data in Table 2 shows, the combination of cyclic 1,3-ketone, aminoalcohol and sodium hydrogen bisulfite leads to drastic reductions in the emitted amounts of all four aldehydes. 

What is claimed is:
 1. A process for producing a polyurethane foam comprising forming a reaction mixture that contains an aromatic polyisocyanate, at least one isocyanate-reactive material having an average functionality of at least 2 and an equivalent weight of at least 200 per isocyanate-reactive group, at least one blowing agent, at least one surfactant and at least one catalyst, and curing the reaction mixture in the presence of (i) at least one cyclic 1,3-diketone, (ii) at least one aminoalcohol and/or alkylhydroxylamine selected from the group consisting of one or more of 2-amino-1-butanol, 2-amino-2-ethyl-1,3-propanediol, 2-amino-2-methyl-1-propanol, 2-amino-1-methyl-1,3-propanediol, 1,1,1-tris (hydroxymethyl) methylamine, N-methylethanolamine, N-butylethanolamine, 2-amino-2(hydroxymethyl)propane-1,3-diol, N-isopropylhydroxylamine, ethylhydroxylamine, methylhydroxylamine, N-butylhydroxylamine and sec-butylhydroxylamine and (iii) an alkali metal, ammonium or phosphonium sulfite, to form the polyurethane foam.
 2. A method for reducing aldehyde emissions from a polyurethane foam, comprising: a) combining (i) at least one cyclic 1,3-diketone, (ii) at least one aminoalcohol and/or alkylhydroxylamine selected from the group consisting of one or more of 2-amino-1-butanol, 2-amino-2-ethyl-1,3-propanediol, 2-amino-2-methyl-1-propanol, 2-amino-1-methyl-1,3-propanediol, 1,1,1-tris (hydroxymethyl) methylamine, N- N-butylethanolamine, monoisopropanolamine, 2-amino-2(hydroxymethyl)propane-1,3-diol, N-isopropylhydroxylamine, ethylhydroxylamine, methylhydroxylamine, N-butylhydroxylamine and sec-butylhydroxylamine and (iii) an alkali metal, ammonium or phosphonium sulfite with at least one isocyanate-reactive material having an average functionality of at least 2 and an equivalent weight of at least 200 per isocyanate-reactive group to form a mixture and then b) combining the mixture from step a) with at least one organic polyisocyanate and curing the resulting reaction mixture in the presence of at least one blowing agent, at least one surfactant and at least one catalyst to form a polyurethane foam.
 3. The process of claim 1 wherein the cyclic 1,3-diketone is represented by structure II

wherein X, Y, Z are independently carbonyl, —C(R²R³)—, —NR⁴—, —O— or a chemical bond, each R² and R³ are independently H, a substituted or unsubstituted linear or branched alkyl or alkenyl group having 1 to 10 carbon atoms, a substituted or unsubstituted phenyl group, a halogen, —CO₂CH₃, or —CN, with the proviso that any two or more of R² and R³ may be connected intra- or inter-molecularly and each R⁴ is independently H, a substituted or unsubstituted linear or branched alkyl or alkenyl group having 1 to 10 carbon atoms or a substituted or unsubstituted phenyl group.
 4. The process of claim 1 wherein the cyclic 1,3-diketone is represented by structure (III):

wherein Z is carbonyl, —C(R²R³)—, —NR⁴—, —O— or a chemical bond, each R² and R³ are independently H, a substituted or unsubstituted linear or branched alkyl or alkenyl group having 1 to 10 carbon atoms, a substituted or unsubstituted phenyl group, a halogen, —CO₂CH₃, or —CN, with the proviso that any two or more of R² and R³ may be connected intra- or inter-molecularly and each R⁴ is independently H, a substituted or unsubstituted linear or branched alkyl or alkenyl group having 1 to 10 carbon atoms or a substituted or unsubstituted phenyl group.
 5. The process of claim 1 wherein the cyclic 1,3-diketone is one or more of cyclohexane-1,3,5-trione, 1,3-cyclohexanedione, pyrazolidine-3,5-dione, 1,2-dimethylpyrazolidine-3,5-dione, 1-methylpyrazolidine-3,5-dione, 1,1-dimethyl-cyclopentan-2,4-dione, 1-ethyl-cyclohexan-2,4-dione, 1, 1-diethyl-cyclohexan-3,5-dione, 6-methyl-pyran-2,4-dione, 6-ethyl-pyran-2,4-dione, 6-isopropyl-pyran-2,4-dione, 6-(n)-butyl-pyran-2,4-dione, 6-isobutyl-pyran-2,4-dione, 6-pentyl-pyran-2,4-dione, 6-isopentyl-pyran-2,4-dione, 6,7-dihydrocyclopenta [b]pyran-2,4(3H, 5H)-dione, 5,6,7,8-tetrahydro-chroman-2,4-dione, chroman-2,4-dione, 6-trans-propenyl-dihydro-pyran-2,4-dione, 1-oxaspiro-[5,5]-undecan-2,4-dione, 2,2-dipropyl-[1,3]-dioxan-4,6-dione, 2-phenyl-[1,3]-dioxan-4,6-dione, 6,10-dioxa-spiro-[4,5]-decan-7,9-dione, 1,5-dioxa-spiro-[5,5]-undecan-2,4-dione, 1-methyl-2,4,6-trioxo-hexahydro-pyrimidine, 1-ethyl-2,4,6-trioxo-hexahydro-pyrimidine, 1-phenyl-2,4,6-trioxo-hexahydro-pyrimidine, s-indacene-1,3,5,7(2H, 6H)-tetraone, furan-2,4 (3H, 5H)-dione, 3,3′-(hexane-1,1-diyl)bis(1-methylpyrimidine-2,4,6 (1H, 3H, 5H)-trione), 2,2-dimethyl-1,3-dioxane-4,6-dione, furan-2,4(3H, 5H)-dione, pyrimidine-2,4,6(1H, 3H, 5H)-trione and 1,3-dimethylpyrimidine-2,4,6(1H, 3H, 5H)-trione.
 6. The process of claim 1 wherein the alkali metal, ammonium or phosphonium sulfite is sodium hydrogen sulfite.
 7. The process of claim 1 wherein the cyclic 1,3-diketone is present in an amount of from 0.03 to 0.25 parts by weight per 100 parts by weight of the at least one isocyanate reactive compound having at least two isocyanate-reactive groups per molecule and an equivalent weight of at least 200 per isocyanate-reactive group.
 8. The process of claim 1 wherein the aminoalcohol alkylhydroxylamine is present in an amount of from 0.05 to 0.25 parts by weight per 100 parts by weight of the at least one isocyanate reactive compound having at least two isocyanate-reactive groups per molecule and an equivalent weight of at least 200 per isocyanate-reactive group.
 9. The process of claim 1 wherein the alkali metal, ammonium or phosphonium sulfite is present in an amount of 0.025 to 0.25 parts by weight per 100 parts by weight of the at least one isocyanate reactive compound having at least two isocyanate-reactive groups per molecule and an equivalent weight of at least 200 per isocyanate-reactive group.
 10. The process of claim 1 wherein the reaction mixture is cured in the presence of an antioxidant.
 11. The process of claim 10 wherein the antioxidant is a phenolic compound.
 12. The process of claim 11 wherein the antioxidant is present in an amount of 0.2 to 1.5 parts by weight per 100 parts by weight of the at least one isocyanate reactive compound having at least two isocyanate-reactive groups per molecule and an equivalent weight of at least 200 per isocyanate-reactive group.
 13. The process of claim 1 wherein the cyclic 1,3-diketone is 1,3-cyclohexanedione.
 14. A process for producing a polyurethane foam comprising forming a reaction mixture that contains an aromatic polyisocyanate, at least one isocyanate-reactive material having an average functionality of at least 2 and an equivalent weight of at least 200 per isocyanate-reactive group, at least one blowing agent, at least one surfactant and at least one catalyst, and curing the reaction mixture in the presence of (i) at least one cyclic 1,3-diketone, (ii) 1,1,1 tris(hydroxymethyl) methylamine and (iii) an alkali metal, ammonium or phosphonium sulfite, to form the polyurethane foam, wherein the reaction mixture is cured in the presence of an antioxidant and the antioxidant is a phenolic compound.
 15. A polyurethane foam made in accordance with the process of claim
 1. 16. A process for producing a polyurethane foam comprising forming a reaction mixture that contains an aromatic polyisocyanate, at least one isocyanate-reactive material having an average functionality of at least 2 and an equivalent weight of at least 200 per isocyanate-reactive group, at least one blowing agent, at least one surfactant and at least one catalyst, and curing the reaction mixture in the presence of (i) at least one cyclic 1,3-diketone, (ii) 1, 1,1 tris(hydroxymethyl) methylamine and (iii) an alkali metal, ammonium or phosphonium sulfite, to form the polyurethane foam.
 17. A polyurethane foam made in accordance with the process of claim
 14. 18. A polyurethane foam made in accordance with the process of claim
 16. 19. The process of claim 1 wherein the aminoalcohol and/or alkylhydroxylamine is selected from the group consisting of N-isopropylhydroxylamine, ethylhydroxylamine, methylhydroxylamine, N-butylhydroxylamine and sec-butylhydroxylamine.
 20. The method of claim 2 wherein the aminoalcohol and/or alkylhydroxylamine is selected from the group consisting of N-isopropylhydroxylamine, ethylhydroxylamine, methylhydroxylamine, N-butylhydroxylamine and sec-butylhydroxylamine. 